치과 수복학에서의 니오븀

The application of metal dental restorations in oral prosthetics has become very widespread and popular. Due to the complexity of the intraoral environment, it has been the focus of research to improve the mechanical and chemical properties, especially the corrosion resistance, to increase the durability of restorations under the premise of ensuring the good biocompatibility of the materials.Haoka et al. tested the electrochemical properties of niobium-containing magnetic attachments, and the results showed that compared with the traditional magnetic attachments, the magnetic attachments made of Pt-30.0mass%Fe-0.6mass%Nb alloys had better corrosion resistance.Lee et al. tested the electrochemical properties of titanium-niobium alloys. Lee et al. tested the structural properties of titanium-niobium alloys and showed that Ti-10Nb and Ti-27.5Nb alloys had the highest strength, while Ot' phase-dominated (17.5Nb, 20Nb) alloys and B-phase-dominated alloys (>30Nb)의 탄성률이 가장 낮았습니다. . 또한, 테스트에 참여한 모든 티타늄-니오븀 합금은 우수한 내식성을 나타냈습니다.

Kikuchiet al. 다양한 니오븀 비중을 함유한 주조 티타늄-니오븀 합금의 기계적 특성을 테스트한 결과, 5wt% 니오븀을 함유한 티타늄 합금의 경도가 크게 향상되었음을 보여주었습니다. 10wt% 이상의 니오븀을 함유한 티타늄 합금은 항복강도와 인장강도가 크게 향상된 반면 연신율은 크게 감소했습니다. 30wt% 니오븀을 함유한 티타늄 합금은 더 높은 경도, 강도 및 탄성 계수를 유지하면서 더 나은 마모 특성을 나타냈습니다. Hu Xin 등의 연구. 또한 고강도, 고탄성률의 티타늄-지르코늄-니오븀-주석 합금은 구강 수복물에 대한 생체 안전성이 우수한 금속 재료이지만 표면 하중이 증가함에 따라 마모 메커니즘이 연마 마모에서 접착 마모로 변경된다는 사실도 확인했습니다.